Q460C High Strength Low Alloy Structural Steel
Compliant with GB/T 1591-2018 | Higher Strength Grade | Hot Rolled (AR) Delivery
4.1 Designation System
Format: Q + Minimum Upper Yield Strength + Delivery Condition Code + Quality Grade (B, C, D, E, F)
Example Q460C: Q = Yield strength, 460 = Minimum yield value (MPa), C = Quality grade C
Note 1: Hot rolled condition (AR/WAR) code can be omitted. Q460C is hot rolled state.
Note 2: Q + minimum upper yield strength + delivery condition code = "Steel grade".
For Z-direction property: Add suffix like Q460CZ25
7.3 Delivery Condition
Q460C steel is supplied in Hot Rolled (AR) condition.
Note: Hot rolled condition includes hot rolled without special rolling and/or heat treatment. Normalized condition includes normalized + tempering; TMCP condition includes TMCP + tempering.
Table 1 Chemical Composition (Ladle Analysis) — Hot Rolled Q460C
| Grade | Quality | C max | Si max | Mn | P max | S max | N max | Alt min | Microalloy | Additional |
|---|---|---|---|---|---|---|---|---|---|---|
| Q460 | C | 0.20 | 0.60 | 1.00-1.70 | 0.030 | 0.030 | 0.015 | 0.015 | Nb/V/Tia | Cr+Mo≤0.30c |
a To improve steel properties, alloying elements (Nb, V, Ti) may be added by agreement. Total microalloy content Nb+V+Ti ≤0.22%.
b For normalized/normalized rolled steel: Al ≥0.015%, Nb+V+Ti ≤0.22%.
c For TMCP steel: Nb ≤0.09%, V ≤0.10%, Ti ≤0.06%, Cr+Mo ≤0.30%.
d Nitrogen content analysis may be omitted if guaranteed by supplier.
e Product analysis tolerance according to GB/T 222.
f For supply of commercial steel billets, lower limit of chemical composition may be agreed upon.
g When thickness direction performance (Z-direction) is required, sulfur content shall comply with GB/T 5313.
Table 2 Carbon Equivalent CEV (max) — Hot Rolled Q460C
| Grade | Quality | ≤30mm | >30-63mm | >63-150mm | >150-250mm | >250-400mm | Note |
|---|---|---|---|---|---|---|---|
| Q460 | C | 0.53 | 0.54 | 0.55 | — | — | b |
a When Si is controlled (e.g., hot dip galvanizing): for Si ≤0.030%, CEV may increase by 0.02%; for Si ≤0.25%, CEV may increase by 0.01%.
b Only applicable for sections and bars.
Table 7 Tensile Properties — Hot Rolled Q460C
| Thickness (mm) | Upper Yield Strength (MPa) min | Tensile Strength (MPa) | Note |
|---|---|---|---|
| ≤16 | 460 | 550-720 | d |
| >16-40 | 450 | ||
| >40-63 | 430 | ||
| >63-80 | 410 | ||
| >80-100 | 410 | 550-720 | |
| >100-150 | 390 | 530-700 | |
| >150-200 | — | — | e |
| >200-250 | — |
* When yield point is not obvious, Rp0.2 may be used instead of upper yield strength.
d For plates and coils with nominal width ≥600mm, transverse specimens; for other steel products, longitudinal specimens.
e Only applicable for sections and bars.
Table 8 Elongation — Hot Rolled Q460C
| Direction | ≤40mm | >40-63 | >63-100 | >100-150 | >150-250 | Note |
|---|---|---|---|---|---|---|
| Longitudinal | 18 | 18 | 17 | 17 | — | f |
| Transverse | 17 | 17 | 16 | 16 | — |
f Only applicable for sections and bars with thickness ≤150mm.
Table 11 Charpy V-Notch Impact Test — Q460C
| Quality Grade | Test Temperature | Longitudinal KV2 (J) min | Transverse KV2 (J) min | Note |
|---|---|---|---|---|
| C | 0°C | 34 | 27 | g |
g For nominal thickness ≥6mm or diameter ≥12mm, impact test shall be performed. Standard specimen: 10×10×55mm. For smaller sizes: 10×7.5×55mm (75% of specified value) or 10×5×55mm (50% of specified value). Impact test takes longitudinal specimens by default. Transverse specimens may be taken by agreement. When the supplier does not specify the test temperature, grade C shall be tested at 0°C.
Table 12 Bending Test (180°) — Q460C
| Thickness (mm) | Bending Diameter D | Note |
|---|---|---|
| ≤16 | D = 2a (a = specimen thickness) | h |
| >16-100 | D = 3a |
h For plates and coils with nominal width ≥600mm, transverse specimens; for other steel products, longitudinal specimens. If the supplier can guarantee bending test qualification, the test may be omitted.
Appendix A International Grade Comparison — Q460C
| GB/T 1591-2018 | EN 10025-2 | EN 10025-3 | EN 10025-4 | ASTM A572 | Previous GB/T 1591-2008 | Note |
|---|---|---|---|---|---|---|
| Q460C (Hot Rolled) | — | — | — | Gr.65 | Q460C (Hot Rolled) | i |
i Q460C offers minimum yield strength of 460MPa with guaranteed impact toughness at 0°C, comparable to ASTM A572 Grade 65. For normalized grade Q460NC and TMCP grade Q460MC, contact Cehe Steel for equivalents (EN 10025-3 S460N/S460NL, EN 10025-4 S460M/S460ML).
CEV formula: CEV(%) = C + Mn/6 + (Cr+Mo+V)/5 + (Ni+Cu)/15
Pcm formula: Pcm(%) = C + Si/30 + Mn/20 + Cu/20 + Ni/60 + Cr/20 + Mo/15 + V/10 + 5B
Note: Carbon equivalent (CEV) based on ladle analysis. When C ≤0.12% in TMCP steel, Pcm may be used instead of CEV.